Model NO.: steel plate
Special Use: High-strength Steel Plate, Wear Resistant Steel
Application: Mining Machiner/Armor Plate/Heavy Duty Machine
Hardness Range: 360hb-600hb
Cutting Service: Avaliable
Bending Service: Avaliable
Hard 500: Hard 400
Armor Steel Plate: Ballistic Plate
Trademark: Shandong
Transport Package: Seaworth Packaging
Specification: thickness: 4.5-150mm
Origin: China
Model NO.: steel plate
Special Use: High-strength Steel Plate, Wear Resistant Steel
Application: Mining Machiner/Armor Plate/Heavy Duty Machine
Hardness Range: 360hb-600hb
Cutting Service: Avaliable
Bending Service: Avaliable
Hard 500: Hard 400
Armor Steel Plate: Ballistic Plate
Trademark: Shandong
Transport Package: Seaworth Packaging
Specification: thickness: 4.5-150mm
Origin: China
Ar400 Ar500 Wear Resistant Plates/Armor Steel Plate/Ballistic Plate
Bulletproof wear resistant steel plateWear  Resistant  Steel plate
Abrasion Resisant Plate AR400 AR500
Hard steel plate
hard 500 hard 400
steel plate cutting and bending
Product Descrition
- Production Process
Blast  Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast
2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment
3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging
4.Thickness  and  Width
Thickness:4.5mm-150mm
Width:1600mm-4100mm
5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500
6.Chemical Composition&Property
| Grade | c | Si | Mn | P | S | Al | Cr+Ni+Mo | Nb+V+Ti |
| NM400 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.9 | Trace Amount |
| NM450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.2 | |
| NM500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.5 | |
| NM550 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Max 0.015 | Max 0.003 | Min 0.020 | Max 2.0 | |
| NM600 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Max 0.015 | Max 0.003 | Min 0.020 | Max 2.5 | |
| XCHD400 | 0.10-0.30 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.1 | |
| XCHD450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.9 | |
| XCHD500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.5 |
7.
Â
| Grade | Size(mm) | RP0.2(Mpa) | Rm(Mpa) | A50(%) | AKV,(ºC) | KV2(J) | HBW | ||
| NM400 | 100 | 1233 | 1337 | 15 | -20 | 35 | 37 | 42 | 415 |
| NM450 | 60 | 1345 | 1434 | 9.5 | -20 | 72 | 59 | 58 | 455 |
| NM500 | 50 | 1608 | 1706 | 10.5 | -20 | 43 | 50 | 45 | 495 |
| XCHD400 | 35 | 1025 | 1161 | 17.5 | -40 | 52 | 45 | 40 | 413 |
| XCHD450 | 30 | 1281 | 1400 | 10.5 | -40 | 45 | 48 | 52 | 453 |
| XCH500 | 6 | 1465 | 1529 | 13.5 | -40 | 24 | 24 | 22 | 515 |
8.Cerifications
9 Classification Society
ISO 9001 Certified
Â
9.Packaging&Shipping
Seaworthy packaging  by  container  or bulk cargo vessel
Delievery time:stock size within 7days;new material within 40days
10.Our services
We    can  cut  and bend steel plate  according  to customer's requriement or drawing,packaging according  to customers' request
11.Application
By adopting the combined chemical composition design of low carbon,low sulfur,low phosphorous and micro-alloy,by applying the offline quenching and other advanced automation technologies,our wear resistant(Abrasion Resisant) plate are popular at home and abroad. Mainly used for thermal Power plant,Coal Mines ,Cement Mills,Loading Machinery,Mining Machinery,Project Machinery.Metallurgical Machinery,Wear resistant plate also can be applied in Sand Mill Cylindrical Shell, Vane, Mechanical Parts used in yard and port, Bearing Structure Parts etc.
12.Our armor steel plate testing results in different thickness
Â
| Testing results of wear resistant steel plates | |||||
| Grade | Thickness(mm) | Hardness/HB | Tenslile strength/MPA | Enlongation | -20ºC Longitudinal Impact Value/J |
| NM400 | 6 | 406 | 1280 | 16 | 76/87/65 |
| NM400 | 20 | 404 | 1260 | 17.5 | 57/57/65 |
| NM400 | 50 | 398 | 1300 | 25.5 | 40/35/45 |
| NM400 | 80 | 417 | 1320 | 23.5 | 48/51/49 |
| NM450 | 6 | 439 | 1320 | 23 | 43/38/30 |
| NM450 | 20 | 448 | 1460 | 24 | 62/52/66 |
| NM450 | 50 | 444 | 1340 | 21 | 35/37/40 |
| NM450 | 80 | 454 | 1410 | 21.5 | 40/41/49 |
| NM500 | 6 | 485 | 1653 | 11.5 | 33/26/32 |
| NM500 | 20 | 505 | 1730 | 17.5 | 36/33/30 |
| NM500 | 50 | 499 | 1569 | 16.5 | 42/38/32 |
| NM500 | 70 | 488 | 1540 | 12.5 | 60/55/64 |
| NM550 | 6 | 540 | 1853 | 10.5 | / |
| NM550 | 20 | 545 | 1855 | 11.5 | / |
| NM550 | 50 | 550 | 1900 | 10.5 | / |
| NM550 | 70 | 545 | 1840 | 12 | / |
| NM600 | 6 | 575 | / | / | / |
| NM600 | 20 | 580 | / | / | / |
| NM600 | 50 | 582 | / | / | / |
| NM600 | 70 | 578 | / | / | / |
Our wear resistant steel plate steel melting
Ar400 Ar500 Wear Resistant Plates/Armor Steel Plate/Ballistic Plate
Bulletproof wear resistant steel plateWear  Resistant  Steel plate
Abrasion Resisant Plate AR400 AR500
Hard steel plate
hard 500 hard 400
steel plate cutting and bending
Product Descrition
- Production Process
Blast  Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast
2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment
3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging
4.Thickness  and  Width
Thickness:4.5mm-150mm
Width:1600mm-4100mm
5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500
6.Chemical Composition&Property
| Grade | c | Si | Mn | P | S | Al | Cr+Ni+Mo | Nb+V+Ti |
| NM400 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.9 | Trace Amount |
| NM450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.2 | |
| NM500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.5 | |
| NM550 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Max 0.015 | Max 0.003 | Min 0.020 | Max 2.0 | |
| NM600 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Max 0.015 | Aluminum Alloy Handle Aluminum Alloy Handle,Circular Door Handle,Invisible Door Handle,Bathroom Glass Door Handle Zhaoqing Muyi Hardware Products Co., Ltd , https://www.muyihardware.com |